3M™ 051135-08277 2-Part Matting Adhesive, 400 ml Cartridge, Part A: Liquid/Part B: Viscous Form, Part A: White/Part B: Dark Green, Part A: 1.288/Part B: 1 to 1.1

Item Code: 3M 051135-08277
Brand: 3M
Mfg Part No: 051135-08277
Manufacturer: 3M
Unit Size: 1

Description

A low viscosity 2-part urethane. Used to saturate fiberglass cloth when preparing backup patches. Can also be used for filling cracks, channels and areas restricting the application of an adhesive bead. Due to its excellent absorption into fiberglass mat or cloth, 3M™ fiberglass matting adhesive is used to saturate fiberglass cloth and/or mat when creating backup patches for sheet molded compound (SMC) and fiber reinforced polyester (FRP). Examples of FRP include fiberglass and Metton® panels. If bonding reinforcement patches to flexible plastics or Metton® use 3M™ polyolefin adhesion promoter, part number 05907 before applying the patch. The following times have been determined with ambient air temperature and substrate temperature at 73 deg F (23 deg C) and are considered typical values. Our fiberglass matting adhesive has a mix nozzle dwell time of 9.5 min, work time of 10 min, sanding time of 45 min and cure time of 45 min. 3M™ is well known among collision repair professionals and others who are committed to helping you restore the beauty and value to your cars and boats. 3M™ fiberglass matting adhesive is another way that 3M™ applies science to life and helps you rediscover the excitement of the vehicles you own.

Features Tech Specs Applications

Features

A high performance low viscosity 2-component urethane adhesive
Used to saturate fiberglass cloth when preparing backup patches
Low viscosity
Metered static mixing
Adhesive is used to saturate fiberglass cloth when preparing backup patches
Secondary use includes filling cracks, channels and areas restricting the application of an adhesive bead
Use with 3M™ 08284 performance manual applicator and 3M™ 08193 static mixing nozzle

Tech Specs

Application Time	10
Base Type	Urethane
Color	Part A: White/Part B: Dark Green
Composition	Part A: Methylene Phenylene Isocyanate Urethane Prepolymer (NJTSRN 04499600-6779), Diisocyanate Polymer, Talc, Aluminum Silicate (NJTSRN 04499600-6789), Thickening Agent (NJTSRN 04499600-6784)/Part B: Polyether Polyol (NJTSRN 04499600-6782), Talc, Polyol (NJTSRN 04499600-6783), Urethane Prepolymer (NJTSRN 04499600-6781), Clay, Sodium Oxide
Container Size	400
Container Type	Cartridge
Curing Time	24
Flash Point	Part A: >383 deg F/Part B: >340 deg F
Form	Part A: Liquid/Part B: Viscous
Odor/Scent	Part A: Slight Isocyanate/Part B: Slight Ammonia
Specific Gravity	Part A: 1.288/Part B: 1 to 1.1
Temperature Rating	-40 to 180
Type	2-Part
UPC	05113508277
Viscosity Rating	Part B: 1400 to 1800 cPs
VOC Content	Part B: 2 g/L