Simpson Strong-Tie Strong-Rod ET-HP22-N ET-HP Epoxy Adhesive, 22 oz Side-By-Side Cartridge, Liquid/Paste Form, Black/White, 1.19/1.36

  • Item Code: SIST ET-HP22-N
  • Brand: Simpson Strong-Tie
  • Mfg Part No: ET-HP22-N
  • Manufacturer: Simpson Strong-Tie
  • Unit Size: 1

Description

ET-HP® is a two-component, high-solids, epoxy-based system for use as a high-strength, non-shrink anchor-grouting material. Resin and hardener are dispensed and mixed simultaneously through the mixing nozzle. ET-HP® is formulated for anchoring threaded rod and rebar into concrete (cracked/uncracked) and masonry.

Features Tech Specs Applications

Features

Back To Top
    • Passed the demanding ICC-ES AC308 adverse-condition tests pertaining to elevated temperatures and long-term sustained loads
    • Code listed under the IBC/IRC for cracked and uncracked concrete per ICC-ES ESR-3372
    • Code listed under the IBC/IRC for masonry per IAPMO UES ER-241
    • Suitable for use under static and seismic loading conditions in cracked and uncracked concrete and masonry
    • Easy hole cleaning no power-brushing required
    • When properly mixed, adhesive will be a uniform gray color
    • For best results store between 45 to 90 deg F
    • Surfaces to receive epoxy must be clean
    • Base material temperature must be 50 deg F or above at the time of installation
    • For best results, material should be 70 to 80 deg F at time of application
    • To warm cold material, store cartridges in a warm, uniformly heated area or storage container
    • Do not immerse cartridges in water to facilitate warming
    • Mixed material in nozzle can harden in 30 min at temperatures of 70 deg F and above
    • The load tables list values based upon results from the most recent testing and may not reflect those in current code reports
    • Use only Simpson Strong-Tie® mixing nozzles in accordance with Simpson Strong-Tie® instructions
    • Modification or improper use of mixing nozzle may impair ET-HP adhesive performance
    • Non-sag or thixotroconsistency
    • 133 deg F heat deflection
    • 168 deg F glass transition temperature
    • 2300 psi at 2 days and 2440 psi at 14 days bond strength

Tech Specs

Back To Top
Applicable Materials Water Saturated Concrete, Solid Brick, Grouted Concrete Block, Unreinforced (URM) Brick, Hollow (Ungrouted) Concrete Block, Cracked Concrete, Hollow Brick and Masonry
Base Type Epoxy
Color Black/White
Composition (Resin White Side)-Bisphenol-A Epoxy Resin, Phenol, Polymer With Formaldehyde, Glycidyl Ether, Butyl Glycidyl Ether, Titanium Dioxide, (Hardener Black Side)- 2-Piperazin-1-Ylethylamine, Bisphenol-A, 2,4,6-Tris-Dimethylaminomethy-Phenol, Nonylphenol, Phenol, Crystalline Silica, Quartz, M-Phenylenebis
Container Size 22
Container Type Side-By-Side Cartridge
Curing Time 24 hr at 70 deg F, 72 hr at 50 deg F
Flash Point 250/225
Form Liquid/Paste
Odor/Scent Ammonia/Sweet
pH Range 6.9/10.2
Series ET-HP®
Specific Gravity 1.19/1.36
VOC Content 3

Applications

Back To Top
Highway/Dot, Brick- Solid, Grouted, Brick- Unreinforced Urm/Concrete Block- Hollow Ungrouted, Concrete- Cracked and Hollow Brick

Related Items

SIST SET-XP10

SIST SET-XP10

Simpson Strong-Tie Strong-Rod SET-XP10 SET-XP High Strength Epoxy Adhesive, 8.5 oz Cartridge, Liquid/Paste Form, Black/Green/White, 1.21/1.59

LEARN MORE